Hot Rolled and Cold Rolled 301 Stainless Steel Strip

Hot Rolled and Cold Rolled 301 Stainless Steel Strip

301 Stainless Steel Strip 301 stainless steel strip has good ductility and can be used in mould goods. Also it can be quickly hardened by mechanical processing. It has good weldability. Its wear resistance and fatigue strength are better than that of 304 stainless steel. Compared with 304, its...
Product description

301 Stainless Steel Strip

301 stainless steel strip has good ductility and can be used in mould goods. Also it can be quickly hardened by mechanical processing. It has  good weldability. Its wear resistance and fatigue strength are better than that of 304 stainless steel. Compared with 304, its content of Cr and Ni is low. And it has magnetism after cold rolling.

 

Chemical Composition(%)

C ≤ 0.15

Si ≤ 1.0

Mn ≤ 2.0

Cr: 16.0~18.0

Ni: 6.0-8.0

S ≤ 0.03

P ≤ 0.045

 

Performance

Tensile Strength ≥520

Elongation Rate(%) ≥40

Hardness HB ≤187 HRB≤90 HV ≤200

Density: 7.93 g·cm-3

Specific Heat : c(20℃)0.502 J·(g·C)-1

Resistivity: 0.73 Ω·mm2·m-1

Melting Point: 1398~1420℃

 

Classification

301 stainless steel strips can be classified as 301 soft steel strip, 301 medium hard steel strip, 301 hard steel strip. It is determined by its chemical composition and processing technology.

 

Mechanical Properties

Tensile Strength σb (MPa):≥520

Offset Yield Strength σ0.2 (MPa):≥205

Elongation Rate δ5 (%):≥40

Reduction of Area ψ (%):≥60

Hardness ≤187HB; ≤90HRB; ≤200HV

Heat Treatment Regime

Heat Treatment Regime: solid solution at 1010~1150℃ and fast cooling

Yield strength of stainless steel (N/mm2)≥ 205

 

Strip Density

Density Value: 7.93

Formula for Weight Calculating

weight(kg)=thickness(mm)*width(m)*length(m)*density value


Hot Tags: Hot Rolled and Cold Rolled 301 Stainless Steel Strip, China, manufacturers, suppliers, wholesale, stock, price
Related Products
Feedback

Copyright © JIANGSU JIANGHEHAI STAINLESS STEEL CO.,LTD All Rights Reserved.Tel: +8613511656218