316 Stainless Steel Sheet

Stocks 316 Stainless steel sheet - an austenitic chrome nickel steel with superior corrosion resistance to that of other chrome nickel steels. Widely used when exposed to chemical corrodents, as well as marine atmospheres. 316 Stainless steel sheet is generally considered non-magnetic, but can become magnetic when cold worked. In 316L or dual grade 316/316L, the carbon content has been lowered to .03% max. for corrosion resistance at heat affected zones from welding.

Features

Rust proof

Strong and sturdy

Stable structure

Durability

Sturdiness

Reasonable rate

Details

Plate - Stanless Steel Plate Full Stock 1mm To 50mm Thickness With-500mm To 1500mm Lenth 200mm To 6000mm Long Plate.

Grades Available:

304, 304l, 309, 310, 310s, 316l, 316ti, 317l, 321, 410, 420, & 430.

Typical Applications for 316 includes

Food Preparation Equipment

Laboratory Benches & Equipment

Coastal Architectural Panelling

Boat Fittings

Chemical Containers

Heat Exchangers

Threaded Fasteners

Springs

Chemical Composition(WT%)

C ≤ 0.08

Si ≤ 1.00

Mn ≤ 2.00

Cr: 16.0 to 18.5

P ≤0.035

S ≤0.030

Ni: 10 to 10.4

Mo: 2.0 to 3.0

Physical Property

Tensile Strength ≥ 520MPa

Yield Strength ≥ 205MPa

Elongation: more than 40%

Thickness Classification

(1) Sheet (0.2mm-4mm)

(2) Medium Plate (3mm-30mm)

(3) Thick Plate (4mm-60mm)

(4) Special Thick Plate (60-115mm)

Maintenance

316 Stainless steel sheetwith the development of the economy has become more extensive, people in daily life with stainless steel, but many people do not know much about the performance of stainless steel, 316 Stainless steel sheetmaintenance will know less. Many people think that stainless steel is never rusty, in fact, stainless steel corrosion resistance is good. The reason is that the surface forms a layer of passivation film, in Nature it in the form of a more stable oxide exists. In other words, stainless steel Although the use of different conditions, oxidation degree is not the same, but ultimately is oxidized, this phenomenon is often called corrosion. The surface of the metal exposed to corrosion in the environment of all electrochemical reactions or chemical reactions, uniform corrosion.

316 Stainless steel sheetsurface passivation film among the weak corrosion resistance of the site, due to the self-excited reaction to form pitting reaction, the formation of small holes, coupled with chloride ions close to form a strong corrosive solution, accelerated corrosion reaction speed. There are intergranular corrosion cracking in stainless steel, all of which have destructive effects on the passivation film on the surface of the stainless steel plate. Therefore, the stainless steel surface must be regularly cleaned and maintained to maintain its gorgeous surface and prolong service life.

316 HL Surface Stainless Steel Sheet

316 2B Surface Stainless Steel Sheet

316 8K Surface Stainless Steel Sheet

316 NO.1 Surface Stainless Steel Sheet